Multi-heater system for growing high quality diamond and a method for growing the same

ABSTRACT

Disclosed herein is an apparatus and method for growing a diamond. The apparatus for growing a diamond comprises: a reaction cell that is configured to grow the diamond therein; a main heater including a main heating surface that is arranged along a first inner surface of the reaction cell; and a sub-heater including a sub-heating surface that is arranged along a second inner surface of the reaction cell, the second inner surface being non-parallel with the first inner surface.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present subject matter relates generally to an apparatus and methodfor growing a diamond, and more specifically to an apparatus and methodfor growing a diamond using a plurality of heaters.

2. Related Art

The synthesis of diamond crystals by high temperature, high pressureprocesses via a temperature gradient method was established by theGeneral Electric Company as described in U.S. Pat. No. 4,034,066. As aresult of subsequent large-scale production by Sumitomo ElectricIndustries, Ltd., as described in U.S. Pat. No. 4,836,881, diamondssynthesized by this method are commercially available as heat sinks,super-precision cutting tools, and other fabricated products. Thediamond growth process using a high temperature, high pressure apparatuscan include a reaction cell which contains (a) graphite as a carbonsource, (b) a diamond seed crystal, and (c) a solvent metal whichseparate the carbon source from the seed crystal.

During the growth of diamond crystals, the carbon source dissolves insolvent metal upon heating, and a temperature gradient exists betweenthe carbon source and the seed crystal, thereby permitting diamondcrystal to grow on seed crystal. The growth rate and the diamond qualitydepend not only on the applied temperature and pressure, but also on thealloy chemistry and core geometry. In addition, the growth rate stronglydepends on the temperature gradient and difference between thedissolution site and growth site. As crystal growth continues, thepositions of the materials shift and change. As a result, thetemperature difference and gradient also changes, which result in eitherslowing down of the growth rate or incorporation of inclusions withinthe grown diamonds.

Conventional processes for growing diamonds adopted a single heatersystem which causes a fixed temperature gradient in the cell. One of theshortcomings of these systems is that the initial growth rate is higherthan later growth rate due to the actual temperature gradient decreasingas the crystal grows. As the crystal reaches a certain size, growth willstop since no temperature gradient exists. Hence, according to theconventional method, in order to increase the productivity, thetemperature gradient must be set as high as possible at the beginning.However, while this conventional method may increase the initial growthrate of diamond, this leads to another disadvantage, i.e., moreinclusions incorporated in the diamond crystals. Thus, to growhigh-quality yellow diamond crystals using a single heater, the growthrate is to be limited, which is normally below 6 mg per hour. But, forcertain chemistries and geometries, it is ideal to start with a slowgrowth rate at the beginning to eliminate the inclusions, and increasethe growth rate later on to increase productivity.

SUMMARY OF THE INVENTION

One of the distinctive aspects of the presently claimed subject matteris to provide a multi-heater system for growing high quality diamond atimproved growth rates. The multi-heater systems disclosed herein havevarious advantages, which include the precise control of temperaturegradients independent of one another, if so desired.

The present subject matter provides an apparatus and method for growinga diamond. According to an aspect of the subject matter, the apparatusincludes a reaction cell that is configured to grow the diamond therein;a main heater including a main heating surface that is arranged along afirst inner surface of the reaction cell; and a sub-heater including asub-heating surface that is arranged along a second inner surface of thereaction cell, the second inner surface being non-parallel with thefirst inner surface.

According to another aspect of the subject matter, the reaction cellcontains therein a multi-layer structure including a diamond seed, themain heater and the sub-heater being configured to heat the multi-layerstructure from different angles.

According to a further aspect of the subject matter, the first innersurface of the reaction cell is arranged approximately orthogonal to thesecond inner surface of the reaction cell.

According to a further aspect of the subject matter, the first heatingsurface of the main heater is cylindrical in shape and the secondheating surface of the sub-heater is in the shape of a disc.

According to a further aspect of the subject matter, the second heatingsurface of the sub-heater includes two electrodes that are approximately180° apart from each other.

According to a further aspect of the subject matter, the apparatusfurther includes a third heater including a third heating surface thatis arranged apart from and in parallel to the first heating surface ofthe main heater.

According to a further aspect of the subject matter, the third heatingsurface of the third heater is in the shape of a ring.

According to a further aspect of the subject matter, the third heaterincludes two electrodes that are approximately 180° apart from eachother.

According to a further aspect of the subject matter, the apparatusfurther includes a fourth heater including a fourth heating surface thatis arranged in the reaction cell on a side opposite the second heatingsurface of the sub-heater.

According to a further aspect of the subject matter, the apparatusfurther includes a fifth heater including a fifth heating surface thatis arranged in parallel with the fourth heating surface of the fourthheater, the fourth and fifth heating surfaces being in disc shape.

According to a further aspect of the subject matter, the first heatingsurface of the main heater is in a cylindrical shape and the thirdheating surface of the third heater is in a ring shape; and wherein thesub-heater, the third heater, and fifth heater are positioned on a topside of the main heater.

According to a further aspect of the subject matter, the apparatusfurther includes a controller that controls the main heater and thesub-heater independently.

According to a further aspect of the subject matter, the main heatingsurface of the main heater contains graphite and the sub-heating surfaceof the sub-heater contains graphite and Molybdenum (Mo).

According to another aspect of the subject matter, the method of growinga diamond in a reaction cell containing a carbon source, a solventmetal, and a diamond seed crystal, includes: controlling a main heaterincluding a main heating surface that is arranged along a first innersurface of the reaction cell in such a way that the main heating surfaceis heated up to allow the carbon source to dissolve in the solventmetal; and controlling a sub-heater including a sub-heating surface thatis arranged along a second inner surface of the reaction cell in such away that the sub-heating surface is heated up to allow the carbon sourceto dissolve in the solvent metal, wherein the second inner surface isnon-parallel with the first inner surface.

According to a further aspect of the subject matter, the method furtherincludes:

after controlling the main heater and the sub-heater, controlling athird heater including a third heating surface that is arranged apartfrom and in parallel to the first heating surface of the main heater insuch a way that the third heating surface is heated up to increase atemperature gradient existing between the carbon source and the diamondseed crystal.

According to a further aspect of the subject matter, the step ofcontrolling the third heater begins after a predetermined time periodafter the step of controlling the main heater begins.

According to a further aspect of the subject matter, the predeterminedtime period is more than 24 hours.

According to a further aspect of the subject matter, the steps ofcontrolling the main heater, sub-heater, and third heater is programmedto achieve an optimized condition for producing high-quality transparentyellow diamond crystals.

According to another aspect of the subject matter, the apparatus forgrowing a diamond, includes: a reaction cell that is configured to growthe diamond therein; a first heater including a first heating surfacethat is arranged along an inner surface of the reaction cell; and asecond heater including a second heating surface that is arrangedsubstantially parallel to the first heating surface of the first heater,the second heating surface being smaller than the first heating surface.

According to a further aspect of the subject matter, the first heatingsurface of the first heater is in cylindrical shape and the secondheating surface of the second heater is arranged outside of the firstheating surface of the first heater so that the first and second heatingsurfaces are overlapped with respect to a central axis of thecylindrical first heating surface.

BRIEF DESCRIPTION OF THE DRAWINGS

These and other aspects of the subject matter will be apparent withreference to the examples in the following description and withreference to the accompanying drawings.

FIG. 1 shows a vertical cross-section view of an embodiment of thepresent subject matter.

FIG. 2 shows a related-art carbon equilibrium phase diagram showing theregion where diamond grows using metal catalyst solvents in highpressure high temperature (HPHT) diamond synthesis (Department ofChemistry Website, University of Bristol, U.K.).

FIG. 3 shows a three-dimensional view of the large and small dies, thecore area as well as the gaps between the dies for the flow of coolingwater.

FIG. 4 schematically shows a multi-heater system with a sub-heater onthe top of the cell, according to a first embodiment of the presentsubject matter.

FIG. 5 schematically shows a multi-heater system with a secondindependent heater on the top of the cell, according to a secondembodiment of the present subject matter.

FIG. 6 schematically shows a multi-heater system with a secondindependent heater on the bottom of the cell, according to a thirdembodiment of the present subject matter.

FIG. 7 schematically shows a multi-heater system with a secondindependent heater on the side of the cell, according to a fourthembodiment of the present subject matter.

FIG. 8 shows the effect of the top sub-heater electric resistance on thegrowth speed of the diamond crystals.

FIG. 9 shows yellow diamond growth curves of the cores with one heaterand the two heaters according to the second embodiment of the presentsubject matter wherein the second heater is on the top side of the cell.

DETAILED DESCRIPTION OF THE INVENTION

The Figures are diagrammatic and not drawn to scale. In the Figures,elements which correspond to elements already described have the samereference numerals.

FIG. 1 shows a vertical cross-section view of an embodiment of thepresent subject matter. In FIG. 1, a split-sphere high pressure, hightemperature (HPHT) apparatus 100 includes a split-sphere growth chamber101 and a plurality of safety clamps 102 on opposite sides of the growthchamber 101. The growth chamber 101 comprises a top half and a bottomhalf, with a cavity defined therein. Large dies 103, small dies 104, anda reaction cell 105 are positioned in the cavity. Between the innersurface of the growth chamber 101 and the large dies 103 is providedrubber membrane (or diaphragm) 107.

In operation of the HPHT apparatus 100, as the top and bottom halves ofthe growth chamber 101 are brought together, pressure is applied to thelarge dies 103, which in turn apply pressure to the small dies 104. Aspressure is applied to the small dies 104, the dies apply pressure tothe reaction cell 105. Prior to being placed in the growth chamber 101,the reaction cell 105 is charged with a graphite source, a diamond seed,and a metal solvent/catalyst mixture used to produce a diamond. Graphitesources, diamond seeds and solvent/metal catalysts are generally knownin the art, and any such material is appropriate for use in theapparatus of the present subject matter.

The HPHT apparatus 100 also contains at least one manifold though whichcooling water 109 can access to the cavity of the growth chamber 101from outside of the apparatus 100, and the cooling water 109 can accessin opposite direction. In the embodiment depicted in FIG. 1, themanifold is at least a two-way manifold, allowing a user to either drawgases and other substances out of the growth chamber 101 or introducedifferent gases or material into the growth chamber 101. For example, auser can remove impurities from the growth chamber 101. Alternatively,the flow can be reversed to introduce an inert gas or some other desiredgas into the growth chamber 101 by way of the manifold. An advantage tousing a manifold rather than multiple inlets is that the number oflocations where the chamber is exposed to contamination is kept to aminimum thereby ensuring that the inside of the reaction cell 105 andthe split sphere chamber 101 can be kept under adequate control.

In the HPHT apparatus 100 disclosed in FIG. 1, the reaction cell 105 isconfigured to contain a diamond seed crystal 10, a carbon source 7, anda catalyst separation layer 9 provided between the diamond seed crystal10 and the carbon source 7 (reference numerals referring to FIG. 4).Crystal growth is caused by extremely high isostatic pressures (i.e.,equal from all sides) and a temperature gradient due to resistanceheating in the reaction cell where the maximum temperature is located atthe carbon source 7 and the minimum temperature at the seed crystal 10.The temperatures and pressures in the reaction cell 105 are in thediamond stable region of the carbon phase diagram as shown in FIG. 2.The pressure created at the core surface is based on the geometry of thedies 103, 104, or more specifically, the decrease in the surface area orinteraction area between the rubber membrane 107 and the large die 103in contrast to the interface area between the small dies 104 and thereaction cell 105. The relationship of the large and small dies 103, 104as well as the reduction in surface area is shown in FIG. 3. Thethree-dimensional view in FIG. 3 also shows the gaps 111 between thedies 103, 104 for allowing cooling water to flow through the system.This design allows the pressure at the rubber membrane to be relativelysmall yet create ultra high isostatic pressure at the core cell 105.

A multi-heater system within a reaction cell includes a main heater inthe shape of a cylinder being made from graphite and additional heatersin the shape of a disc or a ring being made from graphite, Mo, or otherconductors. The system includes a main heater in the shape of a cylinderbeing made from graphite and additional heaters in the shape of a discor a ring being made from graphite and/or Mo. It is understood that thering is generally annular in shape. The multi-heater system has theability to precisely control the temperature gradient and temperatureprofile and thus the crystal growth rate. Four embodiments areillustrated in FIG. 4 to FIG. 7.

FIG. 4 schematically shows the multi-heater system having two heaters, amain heater 204 provided on a side of the reaction cell 105 and asub-heater 203 on the top of the reaction cell 105. The side of thereaction cell 105 is arranged approximately orthogonal to the top of thereaction cell 105. The sub-heater 203 includes two electrodes 201 thatare approximately 180° apart from each other. The embodiment illustratedin FIG. 4 is provided with a couple of Mo rings (electric lead) 201;ZrO₂ caps (press media and heat insulator) 202; a graphite disc(sub-heater) 203; a graphite cylinder (main heater) 204; a MgO cylinder(protector) 205; a CsCl sleeve (protector) 206; a graphite tube (diamondsource) 207; metal solvent 208; a metal foil (protecting seed dissolved)209; a diamond seed 210; a seed pad 211; a metal or graphite disc 212; atop ceramic disc 213; and a container (press media and heat insulator)214. As can be seen, in this embodiment, the main heater 204 is locatedon the side inner surface of the container 214 while the sub-heater 203is located under the ZrO₂ caps 202 but on the top of the top ceramicdisc 213.

FIG. 5 schematically shows a multi-heater system having five heaters, amain heater 304 and a second independent heater 315 provided on a sideof the reaction cell 105, a first sub-heater 317 and a second sub-heater303 on the top of the reaction cell 105, and a third sub-heater 312 onthe bottom of the reaction cell 105. The side of the reaction cell 105is arranged approximately orthogonal to the top of the reaction cell105, and the bottom of the reaction cell 105 is arranged approximatelyorthogonal to the side of the reaction cell 105. The first sub-heater317 includes two electrodes 301 that are approximately 180° apart fromeach other. The second independent heater 315 includes two electrodes316 that are approximately 180° apart from each other. The thirdsub-heater 312 includes a heating surface that is arranged in thereaction cell 105 on a side opposite the heating surface of the firstsub-heater 317. The second sub-heater 303 includes a heating surfacethat is arranged in parallel with the heating surface of the thirdsub-heater 312, the heating surfaces of the second and third sub-heaters303, 312 being in disc shape.

The embodiment illustrated in FIG. 5 is provided with a couple of Morings (electric lead) 301; ceramic caps (press media and heat insulator)302; a BN ring 318; a graphite disc (second sub-heater) 303; a graphitecylinder (main heater) 304; a MgO cylinder (protector) 305; a CsClsleeve (protector) 306; a graphite tube (diamond source) 307; metalsolvent 308; a metal foil (protecting seed dissolved) 309; a diamondseed 310; a seed pad 311; a metal or graphite disc (third sub-heater)312; a graphite disc or ring (first sub-heater) 317; a couple ofgraphite rods (electrical lead for second independent heater) 316; agraphite ring (second independent heater) 315; a top ceramic disc 313;and a container (press media and heat insulator) 314. As can be seen, inthis embodiment, the main heater 304 and the second independent heater315 are located on the side inner surface of the container 314, the mainheater 304 being located below the second independent heater 315, thefirst and second sub-heaters 317, 303 are located under the ceramic caps302, the second sub-heater 303 being located below the first sub-heater317, and the third sub-heater 312 is located on the bottom side of thereaction cell 105.

FIG. 6 schematically shows another embodiment of a multi-heater systemhaving five heaters, a main heater 404 and a second independent heater415 provided on a side of the reaction cell 105, a first sub-heater 403on the top of the reaction cell 105, and a second sub-heater 417 and thethird sub-heater 419 on the bottom of the reaction cell 105. The side ofthe reaction cell 105 is arranged approximately orthogonal to the top ofthe reaction cell 105, and the bottom of the reaction cell 105 isarranged approximately orthogonal to the side of the reaction cell 105.The first sub-heater 403 includes two electrodes 401 that areapproximately 180° apart from each other. The second independent heater415 includes two electrodes 416 that are approximately 180° apart fromeach other. The second sub-heater 417 includes a heating surface that isarranged in the reaction cell 105 on a side opposite the heating surfaceof the first sub-heater 403. The third sub-heater 419 includes a heatingsurface that is arranged in parallel with the heating surface of thesecond sub-heater 417, the heating surfaces of the second and thirdsub-heaters 417, 419 being in disc shape.

The embodiment illustrated in FIG. 6 is provided with a couple of Morings (electric lead) 401; ceramic caps (press media and heat insulator)402; a graphite disc (first sub-heater) 403; a graphite cylinder (mainheater) 404; a top ceramic disc 413; a MgO cylinder (protector) 405; aCsCl sleeve (protector) 406; a graphite tube (diamond source) 407; metalsolvent 408; a metal foil (protecting seed dissolved) 409; a diamondseed 410; a seed pad 411; a graphite ring (second independent heater)415; a couple of graphite rods (electrical lead for second independentheater) 416; a graphite disc or ring (second sub-heater) 417; BN or MgOor salt ring 418; a graphite disc (third sub-heater) 419; and acontainer (press media and heat insulator) 414. As can be seen, in thisembodiment, the main heater 404 and the second independent heater 415are located on the side inner surface of the container 414, the secondindependent heater 415 being located below the main heater 404, thefirst sub-heater 403 is located under the ceramic caps 402, and thesecond and third sub-heaters 417, 419 are located on the bottom side ofthe reaction cell 105, the second sub-heater 417 being located below thethird sub-heater 419.

FIG. 7 schematically shows a further embodiment of a multi-heater systemhaving two heaters, a main heater 504 and a second independent heater515 provided on a side of the reaction cell 105. The heating surface ofthe second independent heater 515 is smaller than that of the mainheater 504. The embodiment illustrated in FIG. 7 is provided with acouple of Mo rings (electric lead) 501; ceramic caps (press media andheat insulator) 502; Mo discs (electric conductor) 503; a MgO cylinder(protector) 505; a graphite cylinder (main heater) 504; a top ceramicdisc 513; a graphite ring (second independent heater) 515; a couple ofgraphite rods (electrical lead for second independent heater) 516; agraphite disc or tube (diamond source) 507; a CsCl sleeve (protector)506; metal solvent 508; a metal foil (protecting seed dissolved) 509; adiamond seed 510; a seed pad 511; and a container (press media and heatinsulator) 514. Also, it is also illustrated that an electricalconnection B between the couple of Mo rings 501 by a main power supply(not shown) and another electrical connection A between the couple ofgraphite rods 516 by a second power supply (not shown). As can be seen,in this embodiment, the main heater 504 and the second independentheater 515 are arranged on the side inner surface of the container 514,wherein the second independent heater 515 is located under the mainheater 504.

There can be two sets of power supply (not shown), one for the mainheater and sub-heater and the other one for a second independent heater.The reaction cell 105 is a ceramic container (primarily zirconia) withone set of electrical contacts on the ends to permit current to flowthrough the reaction cell 105 from the top small die 104 to the bottomsmall die 104, and another set of electric contacts on the sides topermit current to flow through the second independent heater from theright small die to the left small die. The second independent heaterscan be placed at different locations within the cell. It can be locatedat the top as in FIG. 5, the bottom as in FIG. 6, and the side as inFIG. 7 of the cell. The sub-heaters are normally located only at the topand/or the bottom of the cell. The multi-heater system allows control ofthe temperature gradients independent of each other, if so desired. Thesystem has the ability to precisely control the temperature gradient andtemperature profile and thus the crystal growth speed during the HPHTprocess. The graphite heaters inside the reaction cell provide adequatetemperature through resistance heating.

In an experiment, the entire reaction cell was placed in the HPHTapparatus at a pressure between 5.0 and 7.5 GPa and current through themain heater was slowly increased to reach a desired temperature, i.e.,between 1200 and 1700° C. The diamond crystals are produced by atemperature gradient technology. The temperature gradient andtemperature profile throughout the reaction cell can be controlledfurther by the introduction of sub-heaters and second independentheaters with variant resistance. An example of the influence of themodification of top sub-heater electric resistance on the growth rate isgiven in FIG. 8.

With the present design, high quality colorless, green, green-yellow,blue and yellow diamond crystals have been successfully producedrepeatedly at a growth speed up to 15 mg/hour. For yellow crystals, itis desirable to have the sub-heater on the top of the cell as in FIG. 4and the second independent heater on the top as in FIG. 5 or the side asin FIG. 7 of the cell. During the HPHT process, initially, only the mainheater and sub-heaters were used to provide enough power for thecatalyst alloy liquid to melt and dissolve the graphite and the fixedtemperature gradient for diamond to grow. After a certain amount oftime, usually more than 24 hours, a good quality diamond crystal with asize up to 1 ct. will be produced, and then, the second independentheater was used with the main heater and its power was slowly raised toincrease the temperature gradient and thus the growth rate. The powergenerated from the main heater, sub-heaters and second independentheater can be programmed to achieve the optimized conditions for theproduction of high-quality transparent yellow diamond crystals with veryhigh growth rates up to 15 mg/hour.

For the colorless stones, it is desirable to have the second independentheater on the bottom as in FIG. 6 of the cell and the sub-heaters on thetop and the bottom. At the beginning of the HPHT process, both powersupplies were turned on so that the temperature gradient was very smallfor the colorless crystal to grow at very low growth rate, which reducedthe amount of inclusions and defects during the its initial growth.During the process, the power of the second independent heater wasslowly lowered to increase the temperature gradient of the reactioncell. The power generated by the main heater, sub-heaters and secondindependent heaters can be programmed to achieve the optimizedconditions for the production of high-quality transparent colorlessdiamond crystals at a growth rate over 3 mg/hour.

FIG. 9 shows yellow diamond growth curves of the cores with one heaterand the two heaters according to the second embodiment of the presentsubject matter, wherein the second heater is on the top side of thecell. In this experiment, the multi-heater system similar to that shownin FIG. 7 was adopted. After 82 hours, the diamonds grown with twoheaters have better quality and larger weight than the diamonds grownwith only one heater. The detailed conditions used in this experimentare as follows:

-   -   Heating temperature: 1350-1450° C.;    -   The size of the main heater (OD (outer diameter)×ID (inner        diameter)×L (length)): 15.15×16.25×24.00 mm;    -   The size of the second independent heater (OD×ID×L):        17.15×16.25×2.00 mm;    -   Mo rings (electric lead) (OD×ID×L): 8.35×8.25×3.10 mm;    -   Ceramic caps (press media and heat insulator) (OD×L): 17.30×3.10        mm;    -   Mo Discs (electric conductor) (OD×L): 17.30×0.10 mm;    -   MgO cylinder (protector) (OD×ID×L): 14.10×12.20×24.00 mm;    -   Top ceramic disc (OD×L): 12.10×6.80 mm;    -   Graphite rod (electrical lead for second independent heater)        (OD×L): 1.10×3.60 mm;    -   Graphite disc or tube (diamond source) (OD×L): 12.10×4.00 mm;    -   CsCl sleeve (protector) (OD×ID×L): 17.25×15.25×24.00 mm;    -   Metal solvent (OD×L): 12.10×7.00 mm;    -   Metal foil (protecting seed dissolution) (OD×L): 12.10×0.10 mm;    -   Diamond seed: 30 Mesh;    -   Seed pad (OD×L): 12.10×6.40 mm;    -   Container (press media and heat insulator; a rectangular with a        hole) (Width1×Width 2×L×ID): 24.20×24·20×30.50×17.40 mm;    -   The pressure for the experiment: 5.50-6.0 GPa;    -   Material for metal catalyst: Fe—Ni alloy;    -   All the components have the same condition except for the        two-heater system having a secondary heater at the top part of        the core, which is located at a position of 9.0 mm far from the        top of the container.

The experimental results comparing the one heater system versus the twoheater system are shown on Table 1 below:

TABLE 1 Avg. Size Description # of Runs Grade 1 Grade 1, 2 Grade 1, 2, 3cts. One Heater 184 25% 54% 71% 3.36 Two Heaters 3948 43% 67% 79% 3.83

Based on the results above, one of ordinary skill in the art willclearly understands that the qualities of diamonds produced by the twoheater system according to the present subject matter are unexpectedlyhigher than those produced by the one heater system.

Although the subject matter has been described with reference to theillustrated embodiment, the subject matter is not limited thereto. Thesubject matter being thus described, it will be obvious that the samemay be varied in many ways. Such variations are not to be regarded as adeparture from the spirit and scope of the subject matter, and all suchmodifications as would be obvious to one skilled in the art are intendedto be included within the scope of the following claims.

1. An apparatus for growing a diamond, comprising: a reaction cell thatis configured to grow the diamond therein; a main heater including amain heating surface arranged along a first inner surface of thereaction cell; and a sub-heater including a sub-heating surface arrangedalong a second inner surface of the reaction cell, the second innersurface being non-parallel with the first inner surface.
 2. Theapparatus according to claim 1, wherein the reaction cell comprises amulti-layer structure including a diamond seed, the main heater and thesub-heater being configured to heat the multi-layer structure fromdifferent angles.
 3. The apparatus according to claim 1, wherein thefirst inner surface of the reaction cell is arranged approximatelyorthogonal to the second inner surface of the reaction cell.
 4. Theapparatus according to claim 1, wherein the first heating surface of themain heater is cylindrical in shape and the second heating surface ofthe sub-heater is in the shape of a disc.
 5. The apparatus according toclaim 1, wherein the sub-heater includes two electrodes that areapproximately 180° apart from each other.
 6. The apparatus according toclaim 1, further comprising a third heater including a third heatingsurface that is arranged apart from and in parallel to the first heatingsurface of the main heater.
 7. The apparatus according to claim 6,wherein the third heating surface of the third heater is in the shape ofa ring.
 8. The apparatus according to claim 7, wherein the third heaterincludes two electrodes that are approximately 180° apart from eachother.
 9. The apparatus according to claim 6, further comprising afourth heater including a fourth heating surface that is arranged in thereaction cell on a side opposite the second heating surface of thesub-heater.
 10. The apparatus according to claim 9, further comprising afifth heater including a fifth heating surface that is arranged inparallel with the fourth heating surface of the fourth heater, thefourth and fifth heating surfaces being in disc shape.
 11. The apparatusaccording to claim 10, wherein the first heating surface of the mainheater is in a cylindrical shape and the third heating surface of thethird heater is in a ring shape; and wherein the sub-heater, the thirdheater, and fifth heater being on a top side of the main heater.
 12. Theapparatus according to claim 1, further comprising a controller thatcontrols the main heater and the sub-heater independently.
 13. Theapparatus according to claim 1, wherein the main heating surface of themain heater contains graphite and the sub-heating surface of thesub-heater contains graphite and Molybdenum (Mo).
 14. A method ofgrowing a diamond in a reaction cell containing a carbon source, asolvent metal, and a diamond seed crystal, comprising: controlling amain heater including a main heating surface that is arranged along afirst inner surface of the reaction cell in such a way that the mainheating surface is heated up to allow the carbon source to dissolve inthe solvent metal; and controlling a sub-heater including a sub-heatingsurface that is arranged along a second inner surface of the reactioncell in such a way that the sub-heating surface is heated up to allowthe carbon source to dissolve in the solvent metal, wherein the secondinner surface is non-parallel with the first inner surface.
 15. Themethod according to claim 14, further comprising: after controlling themain heater and the sub-heater, controlling a third heater including athird heating surface that is arranged apart from and in parallel to thefirst heating surface of the main heater in such a way that the thirdheating surface is heated up to increase a temperature gradient existingbetween the carbon source and the diamond seed crystal.
 16. The methodaccording to claim 15, wherein the step of controlling the third heaterbegins after a predetermined time period after the step of controllingthe main heater begins.
 17. The method according to claim 16, whereinthe predetermined time period is more than 24 hours.
 18. The methodaccording to claim 15, wherein the steps of controlling the main heater,sub-heater, and third heater is programmed to achieve an optimizedcondition for producing high-quality transparent yellow diamondcrystals.
 19. An apparatus for growing a diamond, comprising: a reactioncell that is configured to grow the diamond therein; a first heaterincluding a first heating surface that is arranged along an innersurface of the reaction cell; and a second heater including a secondheating surface that is arranged substantially parallel to the firstheating surface of the first heater, the second heating surface beingsmaller than the first heating surface.
 20. The apparatus according toclaim 19, wherein the first heating surface of the first heater is incylindrical shape and the second heating surface of the second heater isarranged outside of the first heating surface of the first heater sothat the first and second heating surfaces are overlapped with respectto a central axis of the cylindrical first heating surface.